Õpilane: Berta-Benita Lusmägi Tallinn 2015 SISUKORD SISUKORD ............................................................................................2 SISSEJUHATUS ......................................................................................3 KLAASI TOOTMINE ...............................................................................4 PAKENDIJÄÄTMETE KOGUMIS SÜSTEEMID ............................................5 KLAASI TAASKASUTAMINE SISEKUJUNDUSES ....................................6-7 KOKKUVÕTE .........................................................................................8 KASUTATUD MATERJAL .........................................................................9 2 SISSEJUHATUS Klaas on osa meie keskkonnast. Klaas kui vanim tehismaterjal leiutati V- IV aastatuhandel Egiptuses ja Mesopotaamias. Iidseimad klaasesemed olid
Kristian Nõmmik Klaasimaailm ehituses REFERAAT Õppeaines: Hoone osad Ehitusinstituut Õpperühm: KHE 31 Juhendaja: lektor Jüri Tamm Esitamiskuupäev:................ Üliõpilase allkiri:................. Õppejõu allkiri: .................. Tallinn 2018 SISUKORD 1. KLAASI AJALUGU, KIRJELDUS ............................................................................................4 2. KLAASI KOOSTIS JA VALMISTAMINE ................................................................................6 3. ERINEVAD KLAASTOOTED ...................................................................................................7 3.1 Klaasuksed ................................................................................................................
Klaas Klaas on läbipaistev, suhteliselt tugev, raskesti kuluv, oluliselt inertne ja bioloogiliselt mitteaktiivne materjal, millest saab kujundada väga siledaid ja mitteläbilaskvaid pindu. Need soovitavad omandused on võimaldanud väga paljusid rakendusi (klaasi rakendused).Looduslikku klaasi, näiteks obsidiaani, on kasutatud kiviajast peale. Esimene klaasi valmistamine on teada Vana-Egiptusest umbes 2000 eKr. Klaasi kasutati keraamika ja muude esemete glasuurina. 1. sajandil eKr arendati klaasipuhumise tehnikat. Klaas, mis oli olnud äärmiselt haruldane ja väärtuslik, muutus palju tavalisemaks. Vana-Rooma impeeriumi ajal loodi paljud klaasi vormid spetsiaalselt vaaside ja pudelite jaoks. Tavaline klaas on enamasti amorfne ränidioksiid (SiO2), mis on sama keemiline ühend mis kvarts või polükristallilises vormis liiv. Puhta ränidioksiidi sulamispunkt on umbes
.............................................................5 1.6 Polüestri hooldamine ja säilitamine..................................................................................5 1.7 Märgid tootel.....................................................................................................................5 2. AVONI JUMESTUSKREEM.................................................................................................6 2.1 Klaas..................................................................................................................................6 2.1.1 Klaasi ajalugu.............................................................................................................7 2.1.2 Klaasi omadused........................................................................................................7 2.1.3 Klaasi saamine...................................................................
Iisaku Gümnaasium Andreas Nagel 7.klass Klaas referaat Juhendaja : Aili Reiman Iisaku 2009 Sisukord Klaas.....................................................................................................................................................3 Klaasi ajalugu.......................................................................................................................................3 Looduslik klaas.....................................................................................................................................3 Obsidiaan.........................................................................................................................................3 Tektiidid...........................................................................................................................................4 Fulguriit..................................................
................. Tallinn 2017 SISSEJUHATUS........................................................................................................................................3 1.KLAAS...................................................................................................................................................3 1.1Tavaline klaas........................................................................................................................................4 2.KLAASI KASUTAMINE.......................................................................................................................5 1.1.1Arhitektuur.........................................................................................................................................5 2.1Klaasi funktsioonid..............................................
Klaas Klaas on läbipaistev, suhteliselt tugev, raskesti kuluv, oluliselt inertne ja bioloogiliselt mitteaktiivne materjal, millest saab kujundada väga siledaid ja mitteläbilaskvaid pindu. Need soovitavad omandused on võimaldanud väga paljusid rakendusi (klaasi rakendused). Klaasid on ühtlased amorfsed tahked materjalid, mis tavaliselt tekivad sobiva viskoossusega sulanud materjali väga kiirel jahtumisel, nii et ei jää aega korrapärase kristallvõre moodustumiseks. Tavaline klaas on enamasti amorfne ränidioksiid (SiO2), mis in sama keemiline ühend mis kvarts või polükristallilises vormis liiv. Puhta ränidioksiidi sulamispunkt on umbes 2000 ºC, mistõttu klaasu valmistamisel lisatakse liivale alati veel kaks ainet. Üks on sooda (naatriumkarbonaat Na2CO3) või potas (kaaliumkarbonaat), mis alandab sulamispunkti umbes 1000 ºC-le. Ent sooda muudab klaasi lahustuvaks, seega kasutuks, mistõttu
TALLINNA PEDAGOOGILINE SEMINAR JÄÄTMETE VÄHENDAMINE KODUSES MAJAPIDAMISES LHTT Kerli Loopman Õppejõud: L.Viikman TALLINN 2012 JÄÄTMETE TASAKASUTAMINE Jäätmete taaskasutamine on selline jäätmekäitlustoiming, millega jäätmed, neis sisalduv aine või materjal võetakse kasutusele kas uute toodete valmistamiseks või energia saamiseks. Taaskasutada saab mitmeid inimeste igapäevases kodumajapidamises ning ettevõtluses tekkivaid jäätmeid, nagu näiteks klaas, plastmass, kile, metall, paber, papp ja kartong, puit või biolagunevad jäätmed. Jäätmete taaskasutamisel on mitu head põhjust: 1) Loodusressursside säästmine
Kõik kommentaarid